Technical Data Sheet
LOCTITE® 5910®
January-2009
PRODUCT DESCRIPTION
LOCTITE® 5910® provides the following product
characteristics:
Technology Silicone
Chemical Type Oxime silicone
Appearance (uncured) Black pasteLMS
Components One component - requires no mixing
Viscosity Thixotropic paste
Cure Room temperature vulcanizing (RTV)
Application Sealing
Specific Benefit Excellent resistance to automotive
engine oils.
Typical applications include stamped sheet metal covers
(timing covers and oil sumps) where good oil resistance and
the ability to withstand high joint-movement is required. The
thixotropic nature of LOCTITE® 5910® reduces the migration of
liquid product after application to the substrate.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Specific Gravity @ 20 °C 1.34
Flash Point - See MSDS
Extrusion Rate, g/min:
Pressure 0.62 MPa, time 15 seconds, temperature 25 °C:
Semco Cartridge 300 to 650LMS
TYPICAL CURING PERFORMANCE
Surface Cure
Tack Free Time, minutes:
Cured @ 25 °C / 50±5 % RH ≤40LMS
Cure Speed
The graph below shows shear strength developed with time
on Aluminum lapshears at a bond gap of 0.5 mm. Cure
condition 23±2 °C, 60±5% RH. Strength is determined
according to ISO 4587.
% of Full Cured Strength
Cure Time, days
100
75
50
25
0
0 2 4 6 8 10 12 14 16 18 20 21
Depth of Cure
The depth of cure depends on temperature and humidity.
Depth of cure was measured on strip pulled from a
ramped PTFE mold (maximum depth 10 mm).
The graph below shows the increase in depth of cure with
time at 23±2 °C / 50±5 % RH.
Depth of Cure, mm
Cure Time, days
10
9
8
7
6
5
4
3
2
1
0 1 2 3 4 5 6 7 8 9 10 11 12 13 14
TYPICAL PROPERTIES OF CURED MATERIAL
Cured for 1 week @ 25 °C / 50±5 % RH
Physical Properties:
Shore Hardness, ISO 868, Durometer A 30
Elongation, ISO 37, % ≥400LMS
Tensile Strength, ISO 37 N/mm² ≥1.7LMS
(psi) (≥247)
Tensile Strength, at 100%
elongation, ISO 37
N/mm² 0.6 to 1.0LMS
(psi) (87 to 145)
Electrical Properties:
Volume Resistivity, IEC 60093, Ω·cm 1.69×1014
Surface Resistivity, IEC 60093, Ω 2.81×1016
Dielectric Constant / Dissipation Factor, IEC 60250:
1-kHz 4.53 / 0.019
100-kHz 4.09 / 0.009
1-MHz 4.05 / 0.008
10-MHz 4.08 / 0.017
TYPICAL PERFORMANCE OF CURED MATERIAL
Adhesive Properties
After 21 days @ 23 °C / 60±5% RH and 0.5 mm gap
Lap Shear Strength, ISO 4587:
Mild steel N/mm² 0.9 to 1.4
(psi) (130 to 200)
Aluminum 2024-T3 N/mm² 0.6 to 1.4
(psi) (90 to 200)
Alclad N/mm² 1 to 1.6
(psi) (145 to 230)
TDS LOCTITE® 5910®, January-2009
Zinc dichromate N/mm² 1 to 1.6
(psi) (145 to 230)
TYPICAL ENVIRONMENTAL RESISTANCE
Cured for 21 days @ 23 °C / 60±5% RH
Lap Shear Strength, ISO 4587:
Alclad
Hot Strength
Tested at temperature
% Strength @ 22 °C
Temperature, °C
100
75
50
25
0
0 25 50 75 100 125 150 175 200
Heat Aging
Aged at temperature indicated and tested @ 22 °C
% Strength @ 22 °C
Exposure Time, hours
100
75
50
25
0
0 200 400 600 800 1000
200 °C
Environmental Aging - Effect on bulk properties
Cured for 21 days @ 23±2 °C / 60±5% RH, 2 mm thick film
Tensile strength, ISO 37, N/mm² (Elongation, at break, %):
Environment 100 h 500 h 1000 h
22 °C 1.7(700) 2.4(600) 1.9(560)
150 °C 2.2(400) 2.2(450) 2.3(470)
175 °C 2.2(380) 2.1(350) 1.4(330)
200 °C 2.2(370) 2.0(340) 1.4(300)
5W40 oil, 120 °C 1.9(520) 2.3(490) 2.1(590)
Motor oil, 150°C 1.9(520) 1.8(450) 2.6(600)
Water/glycol 1.0(620) 0.6(540) 0.9(570)
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials
For safe handling information on this product, consult the
Material Safety Data Sheet (MSDS).
Directions for use:
1. For best performance bond surfaces should be clean and
free from grease.
2. Moisture curing begins immediately after the product is
exposed to the atmosphere, therefore parts to be
assembled should be mated within a few minutes after the
product is dispensed.
3. The bond should be allowed to cure (e.g. seven days),
before subjecting to heavy service loads.
4. Excess material can be easily wiped away with non-polar
solvents.
Loctite Material SpecificationLMS
LMS dated January-08, 2009. Test reports for each batch are
available for the indicated properties. LMS test reports include
selected QC test parameters considered appropriate to
specifications for customer use. Additionally, comprehensive
controls are in place to assure product quality and
consistency. Special customer specification requirements may
be coordinated through Henkel Quality.
Storage
Store product in the unopened container in a dry location.
Storage information may be indicated on the product container
labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or
greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during
use. Do not return product to the original container. Henkel
Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than
those previously indicated. If additional information is required,
please contact your local Technical Service Center or
Customer Service Representative.
Conversions
(°C x 1.8) + 32 = °F
kV/mm x 25.4 = V/mil
mm / 25.4 = inches
μm / 25.4 = mil
N x 0.225 = lb
N/mm x 5.71 = lb/in
N/mm² x 145 = psi
MPa x 145 = psi
N·m x 8.851 = lb·in
N·m x 0.738 = lb·ft
N·mm x 0.142 = oz·in
mPa·s = cP
Henkel Americas
+860.571.5100
Henkel Europe
+49.89.320800.1800
Henkel Asia Pacific
+86.21.2891.8863
For the most direct access to local sales and technical support visit:www.henkel.com/industrial
TDS LOCTITE® 5910®, January-2009
Note
The data contained herein are furnished for information only
and are believed to be reliable. We cannot assume
responsibility for the results obtained by others over whose
methods we have no control. It is the user's responsibility to
determine suitability for the user's purpose of any production
methods mentioned herein and to adopt such precautions as
may be advisable for the protection of property and of persons
against any hazards that may be involved in the handling and
use thereof. In light of the foregoing, Henkel Corporation
specifically disclaims all warranties expressed or implied,
including warranties of merchantability or fitness for a
particular purpose, arising from sale or use of Henkel
Corporation’s products. Henkel Corporation specifically
disclaims any liability for consequential or incidental
damages of any kind, including lost profits. The discussion
herein of various processes or compositions is not to be
interpreted as representation that they are free from
domination of patents owned by others or as a license under
any Henkel Corporation patents that may cover such
processes or compositions. We recommend that each
prospective user test his proposed application before repetitive
use, using this data as a guide. This product may be covered
by one or more United States or foreign patents or patent
applications.
Trademark usage
Except as otherwise noted, all trademarks in this document
are trademarks of Henkel Corporation in the U.S. and
elsewhere. ® denotes a trademark registered in the U.S.
Patent and Trademark Office.
Reference 1.4
Henkel Americas
+860.571.5100
Henkel Europe
+49.89.320800.1800
Henkel Asia Pacific



欢迎购买本公司乐泰胶水loctite)产品 ,销售热线:022-58583088

 
Copyright © 2003-2017 乐泰胶水(loctite)中国直销网 All Rights Reserved. ICP备:津ICP备11004391号-3
友情链接: 乐泰胶水 loctite